DEZOGARD E-250
MIO polyamide intermediate epoxy paint
This two-component product, which is obtained from the combination of epoxy resin and polyamide hardener, forms a hard layer on metal surfaces after drying. This coating dries as a result of chemical reactions and is widely used as a protective coating in metal structures, industrial tanks and bridges and other marine facilities, and in cases where high resistance to atmospheric, chemical and mechanical factors is considered. can be used Due to the MIO sheet structure, this coating prevents the penetration of moisture and ions into the lower layer and protects the structure for a long time. Also, the wear and erosion resistance of this coating is very high.
Technical Information:
Gray shade (can be provided in other shades as well)
Mixing ratio = 15/100A/B
Epoxy thinner
Density 1.5 ± 0.1 gr/
Solid weighing 70 ± 2 percent
Volume solid 49 ± 3 percent
cover 7
Surface drying time is less than 6 hours, deep drying time is 24 hours, final drying time is 7 days
Thickness 70 microns
Method of Use:
Considering the importance of the mixing ratio of the components and its effect on the quality of the product, we mix the two components A and B together for 5 minutes with a suitable stirrer until it becomes uniform. After waiting for 30 minutes, it is ready to use.
Surface conditions:
In order to achieve the adhesion of the bister, a lining should be used; The desired surface must be completely clean, dry and free of oil, dust, moisture, salt and other foreign substances to increase the adhesion of the coating and prevent peeling.
Storage time:
One year under standard conditions.
Safety tips:
It is recommended to avoid continuous inhalation of this paint in closed spaces and use appropriate safety equipment as much as possible and wash with plenty of water in case of contact with skin and eyes.
Technical approval:
All the products offered by Iran Technical and Specialized Concrete Clinic are in accordance with international quality standards.